反應性接枝共聚物增容PET/mLLDPE合金的制備及其結構與性能研究

打開文本圖片集

中圖分類號：TQ327.9 文獻標志碼：A 文章編號：1673-3851（2025）07-0451-10

引用格式：，等．反應性接枝共聚物增容PET/mLLDPE合金的制備及其結構與性能研究J].學報（自然科學），2025，53（4）：451-460.

Abstract：To address the compatibility issues between polyethylene terephthalate （PET） and metallocene linear low-density polyethylene （mLLDPE） and to enhance the overall performance of PET/ mLLDPE aloys，PET/mLLDPE alloys were prepared by melt blending with polyolefin elastomer-grafted methacrylic acid glycidyl ester （POE- g GMA） and elastomeric hydrogenated styrene-butadiene block copolymer-grafted methacrylic acid glycidyl ester （SEBS- g GMA） as compatilizers. The impact strength and tensile properties of the PET/mLLDPE alloys were tested using a simply surpported beam impact testing machine and an electronic universal testing machine. The changes in microstructure， carboxyl content at the PET end，thermal properties，and dynamic rheological properties of the PET/mLLDPE alloys before and after compatibilization were characterized using scanning electron microscopy，automatic potentiometric titration，differential scanning calorimetry，and rotational rheometry. The results showed that the PET/mLLDPE/POE- g GMA alloys exhibited superior impact resistance， while the PET/ mLLDPE/SEBS g GMA alloys showed better tensile strength. Both POE- g -GMA and SEBS g -GMA could improve the compatibilityof the PET/mLLDPE alloys，with the former being more effective in refining the size of the dispersed phase mLLDPE. After compatibilization，the storage modulus，loss modulus，and complex viscosity of the PET/mLLDPE alloys all increased， with POE- g -GMA and SEBS- g -GMA contributing significantly to the melt viscosity of the PET/mLLDPE system. These findings provide theoretical reference for the preparation of PET/mLLDPE plastic flooring.

Key words： PET；mLLDPE； reactive compatibilizer; alloy； melt blending； rheological propertie：

0 引言

目前，塑膠地板行業(yè)主要以聚氯乙烯（PVC）板材為主，但PVC地板環(huán)保性較差，燃燒時會釋放有毒物質，如氯化氫（HCD等，對人體健康和環(huán)境造成危害[1]。（剩余14397字）