深水導(dǎo)管架S420高強(qiáng)鋼焊縫金屬擴(kuò)散氫來源及關(guān)鍵影響因素分析

打開文本圖片集

Abstract：The delayed crack of S42O high strength steel in deep-water jacket isvery harmful to the strength and safety of jacket structure because of its concealment.Therefore，it is necessary to strictlycontrol the weld quality of jacket structure.The difusion hydrogen content in weld metal is one of the main causes of delayed cracks.In order to study the influence of construction environment factors （ambient temperature， humidity， wind speed and welding material exposure time）and process parameters （welding heat input and preheating temperature）on the diffusion hydrogen content of weld metal during the welding process of S420 high strength stel for deep-water jacket， this paper used flux-cored wire gas shielded welding （FCAW-G） and submerged arc welding （SAW） processes to test the difusion hydrogen content of S420 high strength steel in different simulated environments.The internal relationship between the source of difusion hydrogen during construction and the actual construction combination conditions and the difusionhydrogencontent of weld metal was studied.By analyzing the sourceand key influencing factors of diffusionhydrogen inthe weld metalofS42Ohigh strength steelfordeep-water jacket，effectivepreventivemeasures were proposed from the perspective of reducing difusion hydrogen content to reduce the probability of delayec cracks in deep-water jacket welding.

eywords： deep-water jacket; S420 high strength steel; environmental factors; welding process; diffusion hyd

1序言

焊接裂紋是深水導(dǎo)管架建造過程中最為嚴(yán)重的焊接缺陷，一直以來都是海洋工程焊接質(zhì)量控制的重點(diǎn)與難點(diǎn)。（剩余8134字）