Pr3+摻雜Ge-As-Ga-Se硫系玻璃和光纖的制備及性能
打開文本圖片集
關(guān)鍵詞：硫系玻璃；稀土摻雜；純化方法；中紅外熒光；中紅外光纖激光中圖分類號：0482.31 文獻(xiàn)標(biāo)識碼：ADOI：10.37188/CJL.20240179 CSTR：32170.14.CJL.20240179
Preparation andPerformance of Doped Ge-As-Ga-Se Chalcogenide Glass and Optical Fiber
WANG Chong'，WUJiahui1，2，GUOHaitao2，TANGYuxin2，XUYantao2* （1.SchoolofElectronicEnginering，Xi’anUniversityofPostsandTelecommunications，Xi’an7Ol21，China; 2.StateKeyLaboratoryofTransient OpticsandPhotonics，Xi’anInstituteofOpticsandPrecision Mechanics， ChineseAcademyofSciences，Xi'an710119，China） ? CorrespondingAuthor，E-mail：xuyantao@opt.ac.cn
Abstract： A 0 . 2 % （mass fraction） high concentration ion doped chalcogenide glass was prepared for gain fibers used in 4 μm wavelength fiber lasers，and a single-mode double cladding gain fiber was fabricatedusing rod-in-tube technology.Theoptical propertiesof theglassand fiberpreparedunderdiferent processes werecomparedandanalyzed byusing X-ray diffraction，diffrential scanningcalorimetry，electron probe element analysis，ellpsometer，infraredthrmalimager，infraredmicroscopy，nfraredFouriertranformspectrometerflu rescence spectrometer，and other methods.The substrate lossof the final preparedoptical fiber is about2.65 dB / m ， and strong fluorescence emission at 3.8-4.8 μ m was successfully detected.This chalcogenide glass fiber has relatively high solubility，good thermal stability and emission property，which has the potential to serve asa gain medium for4 μmband fiber lasers.
KeyWords：chalcogenideglass；rareearthdoping；purification method；mid infraredfluorescence；mid infraredfiber laser
1引言
中紅外波段（ 2 ～ 5 μ m） 激光在國防安全、生物醫(yī)療、先進(jìn)制造等領(lǐng)域都有著重要應(yīng)用。（剩余14080字）